Wear Resistant Extruded Nylon PA6 Plastic Rod

Wear Resistant Extruded Nylon PA6 Plastic Rod   Product performance of pa6 nylon Mechanical properties ​High rigidity: tensile strength 50-80MPa (unreinforced), flexural modulus 2000-3000MPa; after glass fiber reinforcement (such as GF30%), the tensile strength can be increased to 100-150MPa, and the flexural modulus can reach 5000-8000MPa, which is close to the strength level of some aluminum alloys (such as 6061-T6 aluminum alloy tensile strength of about 310MPa), suitable for structural parts with high static loads. ​High impact resistance: cantilever beam notch impact strength ≥5-15kJ/m² (normal temperature), can still maintain good toughness (brittle temperature about -40℃) at low temperature (-20℃), better than HIPS (high impact polystyrene), can withstand dynamic loads or accidental impacts without breaking easily. ​Fatigue resistance: The performance decays slowly under repeated loads (such as dynamic support parts), and the surface hardness (Rockwell R-scale) is about 110-120,…

PTFE Rod PU Sheet ABS Sheet Silicone Sheet POM Sheet